The National Technical Information Service acquires, indexes, abstracts, and archives the largest collection of U.S. government-sponsored technical reports in existence. The NTRL offers online, free and open access to these authenticated government technical reports. Technical reports and documents in its repository may be available online for free either from the issuing federal agency, the U.S. Government Publishing Office’s Federal Digital System website, or through search engines.

Details

Fatigue Crack Propagation from Notched Specimens of 304 SS in an Elevated Temperature Aqueous Environment.

DE2004805335

Publication Date	2002
Personal Author	Wire, G. L.; Mills, W. J.
Page Count	24
Abstract	Fatigue crack propagation (FCP) rates for 304 stainless steel (304SS) were determined in 24 degree C and 288 degree C air and 288 degree C water using double-edged notch (DEN) specimens of 304 stainless steel (304 SS). Test performed at matched loading conditions in air and water at 288 degree C with with 20-60 cc h(sub)2/kg h(sub)2O provided a direct comparison of the relative crack growth rates in air and water over a wide range of crack growth rates. The DEN crack extension ranged from short cracks (0.03-0.25 mm) to long cracks up to 4.06 mm, which are consistent with conventional deep crack tests. Crack growth rates of 304 SS in water were about 12 times the air rate. This 12X environmental enhancement persisted to crack extensions up to 4.06 mm, far outside the range associated with short crack effects. The large environmental degradation for 304 SS crack growth is consistent with the strong reduction of fatigue life in high hydrogen water. Further, very similar environmental effects w ere reported in fatigue crack growth tests in hydrogen water chemistry (HWC). Most literature data in high hydrogen water show only a mild environmental effect for 304 SS, of order 2.5 times air or less, but the tests were predominantly performed at high cyclic stress intensity or equivalently, high air rates. The environmental effect in low oxygen environments at low stress intensity depends strongly on both the stress ratio, R, and the load rise time, T(sub)r, as recently reported for austenitic stainless steel in BWR water. Fractography was performed for both tests in air and water. At 288 degree C in water, the fracture surfaces were crisply faceted with a crystallographic appearance, and showed striations under high magnification. The cleavage-like facets on the fracture surfaces suggest that hydrogen embrittlement is the primary cause of accelerated cracking.
Keywords	Crack propagation Fatigue(Materials) Stainless steels Environmental effects Hydrogen Water chemistry Water Oxygen Pressure vessels
Source Agency	Technical Information Center Oak Ridge Tennessee
Corporate Authors	Bettis Atomic Power Lab., West Mifflin, PA.; Department of Energy, Washington, DC.
Supplemental Notes	Sponsored by Department of Energy, Washington, DC.
Document Type	Technical Report
NTIS Issue Number	200413

Fatigue Crack Propagation from Notched Specimens of 304 SS in an Elevated Temperature Aqueous Environment.

Fatigue Crack Propagation from Notched Specimens of 304 SS in an Elevated Temperature Aqueous Environment.
DE2004805335

Publication Date	2002
Personal Author	Wire, G. L.; Mills, W. J.
Page Count	24
Abstract	Fatigue crack propagation (FCP) rates for 304 stainless steel (304SS) were determined in 24 degree C and 288 degree C air and 288 degree C water using double-edged notch (DEN) specimens of 304 stainless steel (304 SS). Test performed at matched loading conditions in air and water at 288 degree C with with 20-60 cc h(sub)2/kg h(sub)2O provided a direct comparison of the relative crack growth rates in air and water over a wide range of crack growth rates. The DEN crack extension ranged from short cracks (0.03-0.25 mm) to long cracks up to 4.06 mm, which are consistent with conventional deep crack tests. Crack growth rates of 304 SS in water were about 12 times the air rate. This 12X environmental enhancement persisted to crack extensions up to 4.06 mm, far outside the range associated with short crack effects. The large environmental degradation for 304 SS crack growth is consistent with the strong reduction of fatigue life in high hydrogen water. Further, very similar environmental effects w ere reported in fatigue crack growth tests in hydrogen water chemistry (HWC). Most literature data in high hydrogen water show only a mild environmental effect for 304 SS, of order 2.5 times air or less, but the tests were predominantly performed at high cyclic stress intensity or equivalently, high air rates. The environmental effect in low oxygen environments at low stress intensity depends strongly on both the stress ratio, R, and the load rise time, T(sub)r, as recently reported for austenitic stainless steel in BWR water. Fractography was performed for both tests in air and water. At 288 degree C in water, the fracture surfaces were crisply faceted with a crystallographic appearance, and showed striations under high magnification. The cleavage-like facets on the fracture surfaces suggest that hydrogen embrittlement is the primary cause of accelerated cracking.
Keywords	Crack propagation Fatigue(Materials) Stainless steels Environmental effects Hydrogen Water chemistry Water Oxygen Pressure vessels
Source Agency	Technical Information Center Oak Ridge Tennessee
Corporate Authors	Bettis Atomic Power Lab., West Mifflin, PA.; Department of Energy, Washington, DC.
Supplemental Notes	Sponsored by Department of Energy, Washington, DC.
Document Type	Technical Report
NTIS Issue Number	200413